Din Rubber Abrasion Tester
Rubber Testing Equipment
This top quality and highly popular abrasion tester will allow you to measure the abrasion resistance of rubbers (vulcanized thermo set rubbers and thermoplastic elastomers) that are subject to abrasive/frictional wear on their actual service. Since wear is always a result of abrasion, different test methods have been developed for the simulation of long-term wear.
Main Principles:
What a load under a certain level in gauze, grinding a cylindrical cross-section sample determined stroke on the gauze surface, by measuring the amount of wear quality of the sample, and then by the density of the sample to calculate the volume of the amount of abrasion, in order to the test comparable, and finally be subject to the standard rubber, the test results are expressed as relative volumetric wear to verify the amount of gauze-based or full representation with respect to the amount of wear of a certain standard wear rubber base.
Main Feature:
With a small sample, save time, friction way of non-repetition, low noise, high efficiency, good reproducibility and easy to operate and so on.
Din rubber abrasion tester main parameters:
1. The test piece: φ16mm, 6 ~ 15mm (D)
2. Clamp load: 2.5N
3. Weight load: 2.5N, 5N
4. The fixture lateral displacement volume: 4.2mm / wheel every lap
5. Abrasive cloth: 60 #
6. Roller Diameter: 150mm
7. Roller Length: 460mm
8. The roller speed: 40rpm
9. predetermined stroke: 40m / 20m
10. Wear Speed: 0.32m / sec
11. Inclination: 3 ° test piece and the roller support shaft vertical angle
12. Volume: 70 × 30 × 30cm
13. Weight: 61kg
14. Power source: 1∮, AC220V, 3A
Standard：
DIN 53516, JIS K6369 ，GB/T 20991，GB 20265-2006，GB20266-2006，SATRA TM174，BS 903，JIS K6264，GB/T9867，ISO4649
This top quality and highly popular abrasion tester will allow you to measure the abrasion resistance of rubbers (vulcanized thermo set rubbers and thermoplastic elastomers) that are subject to abrasive/frictional wear on their actual service. Since wear is always a result of abrasion, different test methods have been developed for the simulation of long-term wear.
Main Principles:
What a load under a certain level in gauze, grinding a cylindrical cross-section sample determined stroke on the gauze surface, by measuring the amount of wear quality of the sample, and then by the density of the sample to calculate the volume of the amount of abrasion, in order to the test comparable, and finally be subject to the standard rubber, the test results are expressed as relative volumetric wear to verify the amount of gauze-based or full representation with respect to the amount of wear of a certain standard wear rubber base.
Main Feature:
With a small sample, save time, friction way of non-repetition, low noise, high efficiency, good reproducibility and easy to operate and so on.
Din rubber abrasion tester main parameters:
1. The test piece: φ16mm, 6 ~ 15mm (D)
2. Clamp load: 2.5N
3. Weight load: 2.5N, 5N
4. The fixture lateral displacement volume: 4.2mm / wheel every lap
5. Abrasive cloth: 60 #
6. Roller Diameter: 150mm
7. Roller Length: 460mm
8. The roller speed: 40rpm
9. predetermined stroke: 40m / 20m
10. Wear Speed: 0.32m / sec
11. Inclination: 3 ° test piece and the roller support shaft vertical angle
12. Volume: 70 × 30 × 30cm
13. Weight: 61kg
14. Power source: 1∮, AC220V, 3A
Standard：
DIN 53516, JIS K6369 ，GB/T 20991，GB 20265-2006，GB20266-2006，SATRA TM174，BS 903，JIS K6264，GB/T9867，ISO4649
Note：QINSUN is very in place for textile testing and quality control,we have our own textile testing lab. Our textile testing equipment and testing methods are in the leading position in the industry. We have passed the textile testing certification and iso textile testing standards issued by a number of testing,We can provide textile testing equipment pdf manual. Sufficient inventory, big discounts, limited time promotion, Order now!